Resin Pushers - Standard - Tapped Type

Brand :

MISUMI

Caution

Product Description

This is a pusher made of MC nylon polyacetal. It will be installed with female threads. Only tip parts are also available.

Resin Pushers/Standard/Tapped:Related Image

Type		Shape		[ M ]Material
Type		Flat	Round	[ M ]Material
MC Nylon	Tapped	PSHMC	RSHMC	MC Nylon Material: SUS304
MC Nylon	Replacement Resin	MCKK	MCRKK	MC Nylon
Polyacetal	Tapped	PSHPA	RSHPA	Polyacetal Material: SUS304
Polyacetal	Replacement Resin	PAKK	PARKK	Polyacetal

More Information

Specifications
■Properties of MC nylon and polyacetal
• MC nylon: Excels in abrasion resistance compared with polyacetal.
• Polyacetal: Excels in mechanical strength compared with MC nylon.

Item	Abrasion Resistance	Slip Property	Dimensional Stability	Impact Resistance	Flame Resistance	Chemical Resistance.
Item	Abrasion Resistance	Slip Property	Dimensional Stability	Impact Resistance	Flame Resistance	Oil	Acid	Alkali	Organic Solvents
MC Nylon	○	○	△	○	-	○	×	○~△	○
MC Nylon Conductive CDR2	○	○	△	○	-	○	×	○~△	○
Polyacetal	△	○	○	○	[UL94] HB	○	△~×	○	○

Item	Tensile Strength (at ambient temperature)	Elongation	Bending Strength	Compressive Strength		Rockwell Hardness (R Scale)	Continuous Operating Temperature	Volume Specific Resistivity (Ω • cm)	Density	Moisture Absorption
Item	Tensile Strength (at ambient temperature)	Elongation	Bending Strength	Yielding Point	5% Deformation	Rockwell Hardness (R Scale)	Continuous Operating Temperature	Volume Specific Resistivity (Ω • cm)	Density	Water, Balanced	Water, 24hs
Test Method ASTM	D-638		D-790	D-695		D-785	-	D-257	D-792	D-570
MC Nylon	96MPa	30%	110MPa	103MPa	95MPa	120	-40 ~ 120°C	4.2x10¹⁵	1.16	6	0.8
MC Nylon Conductive CDR2	68MPa	10%	117MPa	-	98MPa	119	Room Temperature ~120°C	10²x10⁴	1.20	-	-
Polyacetal	61MPa	40%	89MPa	-	103MPa	119	-45 ~ 95°C	>10¹⁴	1.41	0.7	0.22

[ ! ] For more detailed Properties, see P.953.