Zirconia Balls (Torayceram®)

Standard Unit Price:

SGD 807.00

Days to Ship :

8 Day(s)

[Features]
· TorayCeram (R) bead balls are mainly composed of cubic zirconia that boasts the maximum strength among ceramics by adding yttrium oxide to zirconium oxide.
· Almost no contamination factors such as SiO2, Fe2O3, MgO, etc.

Basic Specifications

• Product Type

  Pot Mill

• Specifications

  Torayceram R

• Manufacturer Product Name

  Zirconia Ball φ0.2

• Hardness

  HV1150-1200

• Diameter(φ mm)

  0.2

• Chemical Composition

  ZrO2 (Contains HfO2): 94.75±0.60 wt%, Y2O3: 4.90±0.50 wt%, Al2O3: 0.30±0.10 wt%

• Application

  Inorganic powder, magnetic paint, ink, pigments, paint and thermosensitive materials for electronic component materials, electronic materials and fine ceramics.

• Density

  6.0g/mL

• Young's Modulus

  210～220GPa

• Bending Strength(MPa)

  1000MPa

• Average crystal grain diameter(μm)

  0.3～0.4μm

• Internal Capacity

  1 Pack (1 kg)